| B - 41 | |||||||||
| PRODUCT CODE NO. OP - 120 R2 | |||||||||
| METALLIZED BOPP CO-EX DRY LAMINATION | |||||||||
| Special BOPP film designed for printing & lamination applications. Good gas barrier property with luxury appearance, heatsealable on non - metallized side. | |||||||||
| TECHNICAL DATA | |||||||||
| TYPICAL PROPERTIES | UNIT | TEST METHODS | TYPICAL VALUE | ||||||
| THICKNESS | micron |
Micrometer |
20 |
25 |
35 |
40 |
|||
| YIELD | m2/ kg (min.) |
- |
55.56 |
44.44 |
31.75 |
27.78 |
|||
| AVERAGE THICKNESS VARIATION | % (max.) |
ASTM E-252 |
± 3 |
± 3 |
± 3 |
± 3 |
|||
| TENSILE STRENGTH | kg/mm2
(min.) |
MD |
ASTM
D-882 |
13 |
13 |
13 |
13 |
||
TD |
24 |
24 |
24 |
24 |
|||||
| ELONGATION AT BREAK | %
(min.) |
MD |
ASTM
D-882 |
200 |
200 |
200 |
200 |
||
TD |
70 |
70 |
70 |
70 |
|||||
| THERMAL SHRINKAGE (120° c 15 minutes) |
%
(max.) |
MD |
ASTM
D-1204 |
4.0 |
4.0 |
4.0 |
4.0 |
||
TD |
2.0 |
2.0 |
2.0 |
2.0 |
|||||
| STATIC C.O.F. | film/film |
ASTM D-1894
|
0.5 - 0.7 |
0.5 - 0.7 |
0.5 - 0.7 |
0.5 - 0.7 |
|||
| SEALING TEMPERATURE | °c |
1 BAR 1 SEC | 125 |
125 |
125 |
125 |
|||
| SEALING STRENGTH | g/cm (min.) |
- |
100 |
100 |
100 |
100 |
|||
| OPTICAL DENSITY | (min.) |
- |
2.0 |
2.0 |
2.0 |
2.0 |
|||
| WVTR | g/m2/24hr
(max.) |
ASTM F-1249 |
3.5 |
3.0 |
2.0 |
1.8 |
|||
| O2TR | cc/m2/24hr
(max.) |
ASTM D-3985 |
400 |
340 |
230 |
200 |
|||
| DESCRIPTION OF SUPPLY | |
| PAPER CORE I.D. | 77 mm (3 in.) 153 mm (6 in.) |
| ROLL O.D. | max. 600 mm |
| WIDTH RANGE | 100 mm - 1,500 mm. (other width on request) |
| LENGTH RANGE | STANDARD 4,000 m., 6,000 m., 12,000 m. (other length on request) |
| JOINT | maximum 10% per order |
| Food approval : complied with FDA & EU regulations (on request) Storage condition : should be keep at ambient temperature ~ 30°c and not over 40°c. and keep in dry storage. |
FURTHER TECHNICAL INFORMATION ON REQUEST The above standard film properties are subjected to change and periodical modification without prior notice, please re-check for the most update version with our Sales & Marketing Department. 12/04/2011 SD-TD-001/31 |