| B - 05 | |||||||||
| PRODUCT CODE NO. OP - 122 R2 | |||||||||
| BOPP PLAIN METALLIZED GRADE | |||||||||
| BOPP non – heatsealable film specially designed for vacuum metallizing application. TFI film offers excellent clarity property. After metallizing process, film provides exceptional shiny metallic appearance with low adhesion of aluminum. | |||||||||
| TECHNICAL DATA | |||||||||
| TYPICAL PROPERTIES | UNIT | TEST METHODS | TYPICAL VALUE | ||||||
| THICKNESS | micron |
Micrometer |
18 |
20 |
25 |
30 |
40 |
50 |
|
| YIELD | m2/kg (min.) |
- |
61.73 |
55.56 |
44.44 |
37.04 |
27.78 |
22.22 |
|
| DENSITY | g/cm3 |
ASTM D-1505 |
0.90 |
0.90 |
0.90 |
0.90 |
0.90 |
0.90 |
|
| AVERAGE THICKNESS VARIATION | % (max.) |
ASTM
E-252 |
± 3 |
± 3 |
± 3 |
± 3 |
± 3 |
± 3 |
|
| TENSILE STRENGTH | kg/mm2
(min.) |
MD |
ASTM
D-882 |
13 |
13 |
13 |
13 |
13 |
13 |
TD |
24 |
24 |
24 |
24 |
24 |
24 |
|||
| ELONGATION AT BREAK | %
(max.) |
MD |
ASTM
D-882 |
170 |
170 |
170 |
170 |
170 |
170 |
TD |
70 |
70 |
70 |
70 |
70 |
70 |
|||
| THERMAL SHRINKAGE
(120°c 15 minutes) |
%
(max.) |
MD |
ASTM
D-1204 |
4.0 |
4.0 |
4.0 |
4.0 |
4.0 |
4.0 |
TD |
2.0 |
2.0 |
2.0 |
2.0 |
2.0 |
2.0 |
|||
| STATIC C.O.F. | film/film |
ASTM D-1894 |
0.4-0.6 |
0.4-0.6 |
0.4-0.6 |
0.4-0.6 |
0.4-0.6 |
0.4-0.6 |
|
| HAZE | % (max.) |
ASTM
D-1003 |
1.5 |
1.5 |
2.0 |
2.0 |
2.0 |
2.0 |
|
| GLOSS (Angle 45°) | % (min.) |
ASTM
D-2457 |
85 |
85 |
85 |
85 |
85 |
85 |
|
| WETTING TENSION | Dyne/cm (min.)
|
ASTM D-2578 |
38 |
38 |
38 |
38 |
38 |
38 |
|
| DESCRIPTION OF SUPPLY | |
| PAPER CORE I.D. | 77 mm (3 in.) 153 mm. (6in.) |
| ROLL O.D. | Max. 800 mm |
| WIDTH RANGE | 100 mm - 1,500 mm. (other width on request) |
| LENGTH RANGE | STANDARD 4,000 m.,- 6,000 m. (other length on request) |
| JOINT | maximum 10% per order |
| Food approval : complied with FDA & EU regulations (on request) Storage condition : should be keep at ambient temperature ~ 30°c and not over 40°c. and keep in dry storage. |
FURTHER TECHNICAL INFORMATION ON REQUEST The above standard film properties are subjected to change and periodical modification without prior notice, please re-check for the most update version with our Sales & Marketing Department. 12/04/2011 SD-TD-001/29 |