| B - 51 | ||||||
| PRODUCT CODE NO. OP - 106 | ||||||
| PROVISIONAL TECHNICAL DATA SHEET | ||||||
| BOPP CO-EX WHITE FILM PRINTING & LAMINATION | ||||||
| It is widely used in surface printing and lamination for packaging applications. Excellent machinability with both sides heatsealable. TFI film shows white appearance. | ||||||
| TECHNICAL DATA | ||||||
| TYPICAL PROPERTIES | UNIT | TEST METHODS | TYPICAL VALUE | |||
| THICKNESS | micron |
Micrometer |
25 |
28 |
35 |
|
| YIELD | m2/kg (min.) |
- |
43.01 |
38.40 |
30.72 |
|
| DENSITY | g/cm3 |
ASTM D-1505 |
0.93 |
0.93 |
0.93 |
|
| AVERAGE THICKNESS VARIATION | % (max.) |
ASTM E-252 |
± 3 |
± 3 |
± 3 |
|
| TENSILE STRENGTH | kg/mm2
(min.) |
MD |
ASTM
D-882 |
8 |
8 |
8 |
TD |
18 |
18 |
18 |
|||
| ELONGATION AT BREAK | %
(max.) |
MD |
ASTM
D-882 |
170 |
170 |
170 |
TD |
70 |
70 |
70 |
|||
| THERMAL SHRINKAGE
(120o c 15 minutes) |
%
(max.) |
MD |
ASTM
D-1204 |
4.0 |
4.0 |
4.0 |
TD |
2.0 |
2.0 |
2.0 |
|||
| STATIC C.O.F. | Film/film |
ASTM D-1894 |
0.35 - 0.50 |
0.35 - 0.50 |
0.35 - 0.50 |
|
| SEALING TEMPERATURE | °c |
1 BAR 1 SEC |
115 |
115 |
115 |
|
| SEALING STRENGTH | g/cm (min.) |
- |
150 |
150 |
150 |
|
| GLOSS (GLOSS SIDE, angle 45° ) | % (min.) |
ASTM D-2457 |
45 |
45 |
45 |
|
| WVTR | g/m2/24hr (max.) |
ASTM F-1249 |
6 |
5 |
4 |
|
| O2TR | cc/m2 /24hr (max.) |
ASTM D-3985 |
1,800 |
1,700 |
1,400 |
|
| WETTING TENSION | Dyne / cm (min.) |
ASTM D-2578 |
38 |
38 |
38 |
|
| DESCRIPTION OF SUPPLY | |
| PAPER CORE I.D. | 77 mm (3 in.) 153 mm (6 in.) |
| ROLL O.D. | max. 800 mm |
| WIDTH RANGE | 100 mm - 1,500 mm. (other width on request) |
| LENGTH RANGE | STANDARD 4,000 M., 6,000 M. (other length on request) |
| JOINT | maximum 10% per order |
| Food approval : complied with FDA & EU regulations (on request) Storage condition : should be keep at ambient temperature ~ 30°c and not over 40°c. and keep in dry storage. |
FURTHER TECHNICAL INFORMATION ON REQUEST The above standard film properties are subjected to change and periodical modification without prior notice, please re-check for the most update version with our Sales & Marketing Department. 31/03/2011 SD-TD-001/12 |