| B - 33 | ||||
| PRODUCT CODE NO. OP - 109A R1 | ||||
| BOPP CO-EX PEARLIZED OPAQUE HIGH GLOSS | ||||
| Is widely used in surface printing and lamination for medium
speed packaging application. Excellent machinability with one side heatsealable
at low temperature. TFI film shows the pearlized white opacity appearance. |
||||
| TECHNICAL DATA | ||||
| TYPICAL PROPERTIES | UNIT | TEST METHODS | TYPICAL VALUE | |
| THICKNESS | Micron |
Micrometer |
25 |
|
| YIELD | m2/kg (min.) |
- |
59.70 |
|
| DENSITY | g/cm3 |
ASTM D-1505 |
0.65-0.70 |
|
| TENSILE STRENGTH | kg/mm2
(min.) |
MD |
ASTM
D-882 |
6 |
TD |
12 |
|||
| ELONGATION AT BREAK | %
(max.) |
MD |
ASTM
D-882 |
140 |
TD |
50 |
|||
| THERMAL SHRINKAGE (120o c 15 minutes) |
%
(max.) |
MD |
ASTM
D-1204 |
4.0 |
TD |
2.0 |
|||
| STATIC C.O.F. | film/film
|
Treated |
ASTM D-1894
|
0.3 - 0.5 |
Untreated |
0.5 - 0.7 |
|||
| SEALING TEMPERATURE | °c |
1 BAR 1 SEC |
115 |
|
| SEALING STRENGTH | g/cm (min.) |
- |
80 |
|
| GLOSS (angle 45° , treated side) |
% (min.) |
ASTM D-2457 |
65 |
|
| WVTR | g/m2/24 hr
(max.) |
ASTM F-1249 |
5.0 |
|
| O2TR | cc/m2/24
hr (max.) |
ASTM D-3985 |
1,700 |
|
| WETTING TENSION | Dyne/cm (min.) |
ASTM D-2578 |
38 |
|
| DESCRIPTION OF SUPPLY | |
| PAPER CORE I.D. | 77 mm (3 in.) 153 mm (6 in.) |
| ROLL O.D. | max. 800 mm |
| WIDTH RANGE | 100 mm - 1,500 mm. (other width on request) |
| LENGTH RANGE | STANDARD 4,000 m., 6,000 m., 8,000 m. (other length on request) |
| JOINT | maximum 10% per order |
| Food approval : complied with FDA & EU regulations (on request)
Storage condition : should be keep at ambient temperature ~ 30oC and not over 40oC. and keep in dry storage.
FURTHER TECHNICAL INFORMATION ON REQUEST The above standard film properties are subjected to change and periodical modification without prior notice, please re-check for the most update version with our Sales & Marketing Department.